ABSTRACT
Commercially available two different compositions of (α+β) brass and lead-tin-brass were annealed, normalized and solution treated at 815°C for 1/2hr. The tensile test data were analyzed to fine the UTS (ultimate tensile strength), elastic modulus, %elongation and reduction in area. The UTS of (α+β) brass with different heat treatments was found to vary between 360.81 to 417.40 MPa with elongation of 8.6-32.0% and between 399.72 to 474.00 MPa with elongation of 4.6-9.9% for lead-tin-brass. The Rockwell hardness (HRF) with these heat treatments was observed to decrease variably for (α+β) brass and also for annealed and normalized samples of lead-tin-brass but increased for solution treated sample.
PDF References Citation
How to cite this article
Abdul Faheem Khan, Anwar Manzoor Rana, Abdus Salam, M. Iqbal Ansari and Nazar Hussain, 2001. Heat Treatment Effects on Mechanical Properties of (α+β) and Lead-tin Brasses. Journal of Applied Sciences, 1: 239-243.
DOI: 10.3923/jas.2001.239.243
URL: https://scialert.net/abstract/?doi=jas.2001.239.243
DOI: 10.3923/jas.2001.239.243
URL: https://scialert.net/abstract/?doi=jas.2001.239.243
REFERENCES
- Padmavardhani, D. and Y.V.R.K. Prasad, 1991. Characterization of hot deformation behavior of brasses using processing maps: Part II. β Brass and α-β brass. Metallurgical Mater. Trans. A, 22: 2993-3001.
CrossRefDirect Link