Articles by Umit Buyuksari
Total Records ( 2 ) for Umit Buyuksari
  Mehmet Akgul , Yalcin Copur , Cengiz Guler , Ayhan Tozluoglu and Umit Buyuksari
  The objective of this study was to investigate the suitability of oak (Ouercus robur L.) wood fibers from Turkey as a raw material for medium density fiberboard. In this study, some of the oak wood parts that are especially not suitable for other forest industries was utilized to produce fiberboards in laboratory environment. Test panels of varying densities (0.6, 0.7 and 0.8 g cm-3) were produced at 18 mm thickness using urea-formaldehyde adhesive. Mechanical, water resistance and dimensional stability properties of the test panels were determined according to Turkish standards. The results indicated that laboratory MDF panels produced using oak fibers resulted in mechanical properties that exceed (except panel type A) levels specified in the appropriate existing standards for the general propose fiberboards.
  Cengiz Guler , Yalcin Copur , Mehmet Akgul and Umit Buyuksari
  The aim of this study was to determine some chemical, physical and mechanical properties of juvenile wood from black pine (Pinus nigra Arnold) plantations. Black pine, one of the important softwood species covers the most of the plantations in Turkey. Black pines that naturally grow in Duzce were 20-23 years old with the dimensions of 13-17 cm utilized in this study. Specimens were prepared and tested according to Turkish standards. The physical properties were measured and air and oven dry wood densities were found to be 0.464 and 0.431 g cm–3, respectively. The volume weight was 0.383 g cm–3. The radial, tangential and volumetric shrinkage values were 4.05, 6.19 and 10.24%, respectively. The radial, tangential and volumetric swelling values were also found to be 3.69, 7.79 and 11.5%, respectively. The mechanical tests resulted in that the static bending and compression strengths were 79.1 and 42.4 N mm–2, respectively. In addition juvenile wood had higher lignin and lower holocellulose content compared to the mature wood. Conclusively, the physical and mechanical properties of juvenile pine wood examined in this study were observed to be lower compared to the mature pine wood.