Articles by Saeid Rafizadeh
Total Records ( 2 ) for Saeid Rafizadeh
  Haleh Kangarlou and Saeid Rafizadeh
  Ti films of the same thickness and near normal deposition angle and the same deposition rate were deposited on glass substrates, at room temperature, under UHV conditions. Due to getting properties of Titanium atoms, they specially react with oxygen during evaporation and TixOy layers produced. Different annealing temperatures as 130 and 330 Celsius degree with uniform 9 cm3 sec-1 oxygen flow, were used for producing titanium di oxide layers. Their nano structures were determined by AFM and XRD methods. Roughness of the films changed due to annealing process. The getting property of Ti and annealing temperature, can play an important role on the nano-structure of the films.
  Saeid Rafizadeh
  Cooper thin films of 54.3 nm thickness were prepared by resistive evaporation method under HV conditions with three different deposition angles namely, vertical, 25° and 35° at the room temperature and on glass substrates. The nano-structures of these layers are studied by AFM and XRD methods. The aim of this research is to investigate correlation between nano-structures and depletion angle in HV condition. All the layers are amorphous and by increasing the depletion angle bigger grains produced and more voids will be configured between them. At vertical depletion angle, roughness of the surface increases and also we encounter with more transmission and less reflection at VIS light wavelength.
 
 
 