  R. J Scougall Vilchis , S Saku , H Kotake and K. Yamamoto
 

The aim of this study was to evaluate the influence of six self-etching primers (SEPs) on the shear/peel bond strength (SPBS) of orthodontic lingual buttons. A total of 150 extracted human premolars were randomly divided into six equal groups. In all groups, the lingual buttons were bonded with BeautyOrtho BondTM and the enamel was conditioned with the following—group I (Control): Primers A & BTM; group II: Transbond Plus SEPTM; group III: Clearfil Mega Bond FATM; group IV: AdheSETM; group V: Peak SE & Peak LC BondTM; and group VI: Bond ForceTM. The teeth were stored at 37°C for 24 hours and the SPBS was tested (0.5 mm/minute). The results were calculated in mega pascals (MPa) and statistically analysed [mean, standard deviation, Scheffè, analysis of variance (P < 0.05)]. The adhesive remnant index (ARI) was also evaluated and statistically analysed with a chi-square test.

All groups demonstrated higher SPBS than the force suggested as necessary to accomplish orthodontic tooth movement, except group IV (7.7 ± 1.7 MPa), which showed a significantly lower value than groups I (10.7 ± 2.4 MPa), II (11.3 ± 3.1 MPa), and V (10.9 ± 2.8 MPa). The values of groups III (9.9 ± 1.6 MPa) and VI (10.5 ± 1.6 MPa) were comparable with those of groups I and V. Significant differences (P < 0.05) were found among the groups in ARI scores.

The SPBS values of all groups could be clinically acceptable and lingual buttons might be successfully bonded with any of these SEPs except AdheSETM since that conditioner significantly influenced bond strength. As the SPBS was lower in all groups than the value at which enamel fractures have been found, a sound enamel surface might be left after removal of lingual buttons.

 
 
 