  Tao Zhu , Weijie Li , Xinghong Zhang , Ping Hu , Changqing Hong and Ling Weng
  ZrB2–10 vol.% SiC ceramics were hot pressed with addition of two contents of ZrO2, i.e., 10 vol.% and 20 vol.%. Oxidation behavior of ZrB2–SiC–ZrO2 ceramics was investigated using muffle furnace in the temperature range of 800–1200 °C in air. With the increase in temperature and extension in holding time, two ceramics both presented more and more severe oxidation behavior. Comparatively, results of microstructure indicated that ceramic with 10 vol.% ZrO2 always exhibited lighter variation in structure after oxidation. Further discussion showed that ceramic with 10 vol.% ZrO2 also provided lower mass gain and thinner oxidized layer. Analysis of oxidation mechanism revealed that excessive addition of ZrO2 brought much path to the inward transport of oxygen and therefore led to the serious oxidation for ZrB2–SiC–ZrO2 ceramics.
  Xinghong Zhang , Lin Xu , Wenbo Han , Ling Weng , Jiecai Han and Shanyi Du
  Hot-pressed zirconium diboride (ZrB2) matrix composites containing 0–30 vol% silicon carbide (SiC) whiskers have been investigated to determine the effect of composition (i.e. amount of SiC whiskers) on the microstructure, mechanical properties and thermal properties. With increasing SiC whisker volume contents, the flexural strength and fracture toughness of the composites were improved compared to those of monolithic ZrB2. Flexural strength increased from 629 MPa for pure ZrB2 to 767 MPa for ZrB2–30 vol%SiCw. Likewise, fracture toughness ranged from 5.4 to 7.1 MPa m1/2 over the same composition range. Specific heat capacity increased with SiC whisker addition, while thermal diffusivity and thermal conductivity decreased slightly with the increase of SiC whisker content.