Articles by Jahimin Asik
Total Records ( 2 ) for Jahimin Asik
  E.B.G. Johnson , Sazmal E. Arshad and Jahimin Asik
  Zeolite A was successfully synthesized from natural kaolin procured from KG. Gading, Bongawan Sabah. The raw kaolin was treated with sodium hexametaphosphate to remove the impurities exist in the natural kaolin. The kaolin clay undergoes metakaolinization at 800°C for 5 h transforming it into highly disordered and amorphous. The raw kaolin and metakaolin were characterized under XRF, XRD and SEM. Reaction mixture for zeolite A was obtained by mixing metakaolin and sodium hydroxide without additional silica. The reaction mixture was stirred for 30 min before hydrothermally synthesised at 100°C for 8 h. Optimum condition for the zeolite A synthesis was studied by preparing reaction mixture with varying molarity. The formation of zeolite A and sodalite was strongly influenced by the molarity of the NaOH used in the reaction mixture.
  Md Lutfor Rahman , Jahimin Asik , Sandeep Kumar and Carsten Tschierske
  Three banana-shaped monomers, i.e. 2,7-naphthalene bis[4-(4-allyloxyphenylazo)-benzoate], 2,7-naphthalene bis[4-(4-allyloxy-3-fluorophenylazo)benzoate] and 2,7-naphthalene bis{4-[4-(10-undecenyloxy)phenylazo]benzoate}, containing azobenzene as side arms, 2,7-dihydroxynaphthalene as central units and terminal double bonds as polymerisable functional groups, were synthesised and their mesophase behaviour investigated. Polarizing optical microscopy and DSC measurements reveal that all compounds exhibit nematic mesophases. The absorption spectrum of the trans-azobenzene groups displays a high-intensity π-π* transition at about 365 nm and a low-intensity n-π* transition at around 450 nm for all compounds. Hence, photochromism can be achieved by the introduction of the azo linkage to banana-shaped liquid crystals molecules.
 
 
 