Abstract: It was observed that no change in fracture mode from microvoid coalescence with hydrogen charging in tin brass tested in impact loading. However, the fracture surface of the hydrogen charged tin brass showed fine and shallow dimples, whereas further charging led to the formation of large flat facets. Moreover, the Charpy V-notch impact energy absorbed by the material is reduced by hydrogen charging.